| As welded | |||||
| Elongation | Tensile Strength | Yield Strength | 保護(hù)氣體 | Stress Relieved Temperature | Stress Relieved Testing Time |
| 27 % | 630 MPa | 540 MPa | ISO | - | - |
| Stress relieved | |||||
| Elongation | Tensile Strength | Yield Strength | 保護(hù)氣體 | Stress Relieved Temperature | Stress Relieved Testing Time |
| - | - | - | AWS | 620 °C | 1 hr |
| As welded | ||||
| Impact Value | Testing Temperature | 保護(hù)氣體 | Stress Relieved Testing Temp | Stress Relieved Testing Time |
| 130 J | -60 °C | ISO | - | - |
| 110 J | -75 °C | ISO | - | - |
| Stress relieved | ||||
| Impact Value | Testing Temperature | 保護(hù)氣體 | Stress Relieved Testing Temp | Stress Relieved Testing Time |
| - | -75 °C | AWS | 620 °C | 1 hr |
| Mn | |||||
| Mn | Mo | C | Si | Ni | Cr |
| 0.8 % | - | - | - | - | - |
| Mo | |||||
| Mn | Mo | C | Si | Ni | Cr |
| - | 0.01 % | - | - | - | - |
| C | |||||
| Mn | Mo | C | Si | Ni | Cr |
| - | - | 0.06 % | - | - | - |
| Si | |||||
| Mn | Mo | C | Si | Ni | Cr |
| - | - | - | 0.36 % | - | - |
| Ni | |||||
| Mn | Mo | C | Si | Ni | Cr |
| - | - | - | - | 3.37 % | - |
| Cr | |||||
| Mn | Mo | C | Si | Ni | Cr |
| - | - | - | - | - | 0.05 % |
| Fusion time per electrode at 90% I max | kg weld metal/kg electrodes | Number of electrodes/kg weld metal | 安培 | 熔敷率 | 電壓 V | 直徑 |
| 60 sec | 0.60 kg | 76.0 | 70-110 A | 0.80 kg/h | 25 V | 2.5 x 350 mm |
| 77 sec | 0.60 kg | 37.0 | 80-150 A | 1.50 kg/h | 25 V | 3.2 x 450 mm |
| 88 sec | 0.63 kg | 26.0 | 90-190 A | 1.80 kg/h | 27 V | 4.0 x 450 mm |
| 100 sec | 0.60 kg | 15.0 | 110-240 A | 2.10 kg/h | 29 V | 5.0 x 450 mm |